1. Study on damage propagation of CA mortar layer for CRTS II slab ballastless track under vehicle-induced hydrodynamic pressure NSTL国家科技图书文献中心

Zhao, Jia | Zhao, Weigang ... - 《Engineering failure analysis》 - 2025,171 - 109356～ - 共20页

摘要：The interlayer damage* propagation in* | damage propagation in CRTS II slab ballastless tracks | damage propagation in CA mortar layers was established | . Damage* propagation indices were proposed, and the* | on damage* propagation was systematically*

关键词： Hydrodynamic pressure | Ballastless track | CA mortar layer | Cracks | Voids | Damage propagation

2. Investigation on Induced Intra/Interlaminar Damage Propagation in CFRP Subjected to Cyclic Tensile Loading After Impact (TAI) NSTL国家科技图书文献中心

Francisco Maciel Mon... | Felipe Ruivo Fuga ... - 《Advances in Mechanical and Power Engineering II》 - International Conference on Advanced Mechanical and Power Engineering - 2025, - 227～236 - 共10页

摘要： the interlaminar damage* propagation, while the* | Impact damage* to composite structures results* | issue, the present study investigates the damage | propagation behaviour with particular emphasis on intra-and | damage modes and extents within the specimens. A non

关键词： Fatigue | Crack propagation | Finite fracture mechanics | Polymer composite

3. Damage mechanism study of TC17 titanium alloy during high-cycle fatigue crack initiation and propagation NSTL国家科技图书文献中心

Lu, Yanli | Lu, Yunmei ... - 《Journal of Alloys and Compounds》 - 2025,1020 - 179549～ - 共18页

摘要：This paper investigated the fatigue damage | mechanisms during crack initiation and propagation* by* | propagation zone, reflected the crack propagation rate | , which indicated that fatigue crack propagation* was* | mechanism of fatigue damage* in TC17 titanium alloy and*

关键词： TC17 titanium alloy | High cycle fatigue | Crack initiation and propagation | Fatigue damage

4. An aircraft structural risk assessment method considering fatigue crack propagation based on fatigue damage diagnosis and prognosis NSTL国家科技图书文献中心

Liang Han | Xiaofan He ... - 《International Journal of Fatigue》 - 2025,190(Jan.) - 108650.1～108650.16 - 共16页

摘要： based on fatigue damage* diagnosis and prognosis has* | been developed, considering fatigue crack propagation | Bayesian Network (DBN) improve crack propagation | An aircraft structural risk assessment method | . The process is divided into three stages: initial

关键词： Risk assessment | Structural prognostics and health management | Fatigue damage diagnosis and prognosis | Crack propagation | Single Flight Probability of Failure

5. Damage Analyses and Crack Propagation of Wire Drawing With Central Inclusion Under Different Compression Ratios NSTL国家科技图书文献中心

Ao Ma | Feng Fang ... - 《Fatigue & Fracture of Engineering Materials & Structures》 - 2025,48(6) - 2743～2758 - 共16页

摘要： crack propagation* caused by damage is realized in the* | . The research on the mechanism of crack propagation | caused by drawing damage* is still to be urgently solved* | -shaped crack propagation* path at the front of the* | under the total drawing strain, the internal damage

关键词： compression ratio | crack propagation | plastic deformation | small size inclusion | steel cord

6. Mechanisms and Damage-Based Assessment of Time-Dependent Fatigue Crack Propagation in Polymer Electrolyte Membrane NSTL国家科技图书文献中心

Liang Cai | Wei Li ... - 《Fatigue & Fracture of Engineering Materials & Structures》 - 2025,48(4) - 1461～1478 - 共18页

摘要：The time-dependent fatigue crack propagation | loading frequency significantly increases the damage | dominant fatigue crack propagation* mode. Then, a cyclic* | loading frequency, thus imposing more damage | assessing fatigue crack propagation* rate under distinct*

关键词： cyclic cohesive zone | cyclic plasticity | damage accumulation | in-situ | loading frequency | polymer electrolyte membrane

7. A nonlocal macro-meso-scale damage model based modeling for crack propagation in ferroelectric materials NSTL国家科技图书文献中心

Xue, Feng | Wang, Jingyu ... - 《Engineering Fracture Mechanics》 - 2025,314 - 110712～ - 共21页

摘要： consistent damage* (NMMD) model has been proposed for* | simulating the crack propagation* in brittle materials* | for microscopic damage* and devised a simple and* | crack propagation* for ferroelectric materials under* | induced geometric damage* is accounted for crack*

关键词： Comsol implementation | Macro-meso-scale consistent damage model | Ferroelectric materials | Electromechanical loading

8. Connecting macroscopic mechanical models to micromechanical phenomena in the failure analysis of a large-diameter prestressed concrete cylinder pipeline NSTL国家科技图书文献中心

Schouwenaars, Rafael | Cueva, Ignacio ... - 《Engineering failure analysis》 - 2025,172 - 109424～ - 共19页

摘要： analyse the damage* propagation leading to catastrophic* | work as a tool for the prediction of damage | propagation under specific environmental, operational and | Large-diameter prestressed concrete cylinder | pipelines for potable water are of crucial importance for

关键词： Prestressed concrete pipeline | Damage propagation | Stress corrosion cracking | Hydrogen embrittlement | Shear lag model

9. An adaptive mesh refinement algorithm for crack propagation with an enhanced thermal-mechanical local damage model NSTL国家科技图书文献中心

Manh Van Pham | Minh Ngoc Nguyen ... - 《Finite elements in analysis & design》 - 2025,243(Jan.) - 104278.1～104278.34 - 共34页

摘要： effective approach for crack propagation* under mechanical* | developed enhanced local damage* model. The mesh-dependent* | and element characteristic length into the damage | derived from the bi-energy norm concept and a new damage | -local/gradient damage* and phase field method. In the*

关键词： Adaptive mesh refinement | Laplace shape function | Enhanced local continuum damage | Staggered scheme

10. Evolution of Unstable Skin-Stringer Debonding Propagation in Composite Aircraft Structures: Implications on Damage Tolerant Design NSTL国家科技图书文献中心

Aniello Riccio | Mauro Zarrelli ... - 《Dynamic Response and Failure of Composite Materials》 - International Symposium on Dynamic Response and Failure of Composite Materials - 2025, - 19～25 - 共7页

摘要：, unstable propagation* of delamination damage is still the* | unsteady and sudden propagation* of skin-stringer* | Interlaminar damages are a key challenge that | limits the widespread use of composite materials in | aircraft primary structural parts. Although years have

摘要：The interlayer damage* propagation in* | damage propagation in CRTS II slab ballastless tracks | damage propagation in CA mortar layers was established | . Damage* propagation indices were proposed, and the* | on damage* propagation was systematically*

关键词： Hydrodynamic pressure | Ballastless track | CA mortar layer | Cracks | Voids | Damage propagation

摘要： the interlaminar damage* propagation, while the* | Impact damage* to composite structures results* | issue, the present study investigates the damage | propagation behaviour with particular emphasis on intra-and | damage modes and extents within the specimens. A non

关键词： Fatigue | Crack propagation | Finite fracture mechanics | Polymer composite

摘要：This paper investigated the fatigue damage | mechanisms during crack initiation and propagation* by* | propagation zone, reflected the crack propagation rate | , which indicated that fatigue crack propagation* was* | mechanism of fatigue damage* in TC17 titanium alloy and*

关键词： TC17 titanium alloy | High cycle fatigue | Crack initiation and propagation | Fatigue damage

摘要： based on fatigue damage* diagnosis and prognosis has* | been developed, considering fatigue crack propagation | Bayesian Network (DBN) improve crack propagation | An aircraft structural risk assessment method | . The process is divided into three stages: initial

关键词： Risk assessment | Structural prognostics and health management | Fatigue damage diagnosis and prognosis | Crack propagation | Single Flight Probability of Failure

摘要： crack propagation* caused by damage is realized in the* | . The research on the mechanism of crack propagation | caused by drawing damage* is still to be urgently solved* | -shaped crack propagation* path at the front of the* | under the total drawing strain, the internal damage

关键词： compression ratio | crack propagation | plastic deformation | small size inclusion | steel cord

摘要：The time-dependent fatigue crack propagation | loading frequency significantly increases the damage | dominant fatigue crack propagation* mode. Then, a cyclic* | loading frequency, thus imposing more damage | assessing fatigue crack propagation* rate under distinct*

关键词： cyclic cohesive zone | cyclic plasticity | damage accumulation | in-situ | loading frequency | polymer electrolyte membrane

摘要： consistent damage* (NMMD) model has been proposed for* | simulating the crack propagation* in brittle materials* | for microscopic damage* and devised a simple and* | crack propagation* for ferroelectric materials under* | induced geometric damage* is accounted for crack*

关键词： Comsol implementation | Macro-meso-scale consistent damage model | Ferroelectric materials | Electromechanical loading

摘要： analyse the damage* propagation leading to catastrophic* | work as a tool for the prediction of damage | propagation under specific environmental, operational and | Large-diameter prestressed concrete cylinder | pipelines for potable water are of crucial importance for

关键词： Prestressed concrete pipeline | Damage propagation | Stress corrosion cracking | Hydrogen embrittlement | Shear lag model

摘要： effective approach for crack propagation* under mechanical* | developed enhanced local damage* model. The mesh-dependent* | and element characteristic length into the damage | derived from the bi-energy norm concept and a new damage | -local/gradient damage* and phase field method. In the*

关键词： Adaptive mesh refinement | Laplace shape function | Enhanced local continuum damage | Staggered scheme

摘要：, unstable propagation* of delamination damage is still the* | unsteady and sudden propagation* of skin-stringer* | Interlaminar damages are a key challenge that | limits the widespread use of composite materials in | aircraft primary structural parts. Although years have

关键词： Composite panel | Unstable delamination | Lock-in thermography | Compressive test | VCCT | FEM

4008-161-200 800-990-8900

国家科技图书文献中心

摘要：The interlayer damage propagation in | damage propagation in CRTS II slab ballastless tracks | damage propagation in CA mortar layers was established | . Damage propagation indices were proposed, and the | on damage propagation was systematically

关键词： Hydrodynamic pressure | Ballastless track | CA mortar layer | Cracks | Voids | Damage propagation

摘要： the interlaminar damage propagation, while the | Impact damage to composite structures results | issue, the present study investigates the damage | propagation behaviour with particular emphasis on intra-and | damage modes and extents within the specimens. A non

关键词： Fatigue | Crack propagation | Finite fracture mechanics | Polymer composite

摘要：This paper investigated the fatigue damage | mechanisms during crack initiation and propagation by | propagation zone, reflected the crack propagation rate | , which indicated that fatigue crack propagation was | mechanism of fatigue damage in TC17 titanium alloy and

关键词： TC17 titanium alloy | High cycle fatigue | Crack initiation and propagation | Fatigue damage

摘要： based on fatigue damage diagnosis and prognosis has | been developed, considering fatigue crack propagation | Bayesian Network (DBN) improve crack propagation | An aircraft structural risk assessment method | . The process is divided into three stages: initial

关键词： Risk assessment | Structural prognostics and health management | Fatigue damage diagnosis and prognosis | Crack propagation | Single Flight Probability of Failure

摘要： crack propagation caused by damage is realized in the | . The research on the mechanism of crack propagation | caused by drawing damage is still to be urgently solved | -shaped crack propagation path at the front of the | under the total drawing strain, the internal damage

关键词： compression ratio | crack propagation | plastic deformation | small size inclusion | steel cord

摘要：The time-dependent fatigue crack propagation | loading frequency significantly increases the damage | dominant fatigue crack propagation mode. Then, a cyclic | loading frequency, thus imposing more damage | assessing fatigue crack propagation rate under distinct

关键词： cyclic cohesive zone | cyclic plasticity | damage accumulation | in-situ | loading frequency | polymer electrolyte membrane

摘要： consistent damage (NMMD) model has been proposed for | simulating the crack propagation in brittle materials | for microscopic damage and devised a simple and | crack propagation for ferroelectric materials under | induced geometric damage is accounted for crack

关键词： Comsol implementation | Macro-meso-scale consistent damage model | Ferroelectric materials | Electromechanical loading

摘要： analyse the damage propagation leading to catastrophic | work as a tool for the prediction of damage | propagation under specific environmental, operational and | Large-diameter prestressed concrete cylinder | pipelines for potable water are of crucial importance for

关键词： Prestressed concrete pipeline | Damage propagation | Stress corrosion cracking | Hydrogen embrittlement | Shear lag model

摘要： effective approach for crack propagation under mechanical | developed enhanced local damage model. The mesh-dependent | and element characteristic length into the damage | derived from the bi-energy norm concept and a new damage | -local/gradient damage and phase field method. In the

关键词： Adaptive mesh refinement | Laplace shape function | Enhanced local continuum damage | Staggered scheme

摘要：, unstable propagation of delamination damage is still the | unsteady and sudden propagation of skin-stringer | Interlaminar damages are a key challenge that | limits the widespread use of composite materials in | aircraft primary structural parts. Although years have

关键词： Composite panel | Unstable delamination | Lock-in thermography | Compressive test | VCCT | FEM

4008-161-200 800-990-8900

国家科技图书文献中心

摘要：The interlayer damage* propagation in* | damage propagation in CRTS II slab ballastless tracks | damage propagation in CA mortar layers was established | . Damage* propagation indices were proposed, and the* | on damage* propagation was systematically*

摘要： the interlaminar damage* propagation, while the* | Impact damage* to composite structures results* | issue, the present study investigates the damage | propagation behaviour with particular emphasis on intra-and | damage modes and extents within the specimens. A non

摘要：This paper investigated the fatigue damage | mechanisms during crack initiation and propagation* by* | propagation zone, reflected the crack propagation rate | , which indicated that fatigue crack propagation* was* | mechanism of fatigue damage* in TC17 titanium alloy and*

摘要： based on fatigue damage* diagnosis and prognosis has* | been developed, considering fatigue crack propagation | Bayesian Network (DBN) improve crack propagation | An aircraft structural risk assessment method | . The process is divided into three stages: initial

摘要： crack propagation* caused by damage is realized in the* | . The research on the mechanism of crack propagation | caused by drawing damage* is still to be urgently solved* | -shaped crack propagation* path at the front of the* | under the total drawing strain, the internal damage

摘要：The time-dependent fatigue crack propagation | loading frequency significantly increases the damage | dominant fatigue crack propagation* mode. Then, a cyclic* | loading frequency, thus imposing more damage | assessing fatigue crack propagation* rate under distinct*

摘要： consistent damage* (NMMD) model has been proposed for* | simulating the crack propagation* in brittle materials* | for microscopic damage* and devised a simple and* | crack propagation* for ferroelectric materials under* | induced geometric damage* is accounted for crack*

摘要： analyse the damage* propagation leading to catastrophic* | work as a tool for the prediction of damage | propagation under specific environmental, operational and | Large-diameter prestressed concrete cylinder | pipelines for potable water are of crucial importance for

摘要：, unstable propagation* of delamination damage is still the* | unsteady and sudden propagation* of skin-stringer* | Interlaminar damages are a key challenge that | limits the widespread use of composite materials in | aircraft primary structural parts. Although years have